Slurry Pump Spare Parts Material Specification

2025-04-18

一、Metal Materials

Common metal parts in Warman slurry pumps include impellers, F.P.L Insert , volute liners, and throat bushings. These parts are exposed to highly abrasive slurries and are typically made of high chrome alloy for superior wear resistance. Structural parts such as casing and bearing housings are usually made of grey or ductile iron.

NO.	China Code	Parts Name	Warman code	U.S.A Code	Performance&Application
METAL	HT200 Grey Iron	Casing,Frame Bearing Housing, Stuffing Box	G01	AWSNO.30
	QT500-7 Ductile Iron	Casing,Frame Bearing Housing	D21	AWS 80-55-06
	KmTBCr26 High Chrome Alloy	Impeller,Volute Liner Trhoat Busing,Expeller F.P.L Insert	A05	ASTM 25%Cr ClassⅢ Type A	Abrasion-resistant performance ower than A07 Fair corrosion-resistance. High impact load abrasion condition.PH range from 5~12
		Impeller,Volute Liner Trhoat Busing,Expeller, F.P.L Insert	A07		Best abrasion-resistant performance;Corrosion resistance performance is inferior than A05. High impact load abrasion condition.
		Impeller,Volute Liner, Trhoat Busing,Expeller, F.P.LInsert	A49	ASTMA532 ClassⅢ Type A	Fair abrasion-resistant performance is 20%less than A05.Fair corrosion resistance performance in media with low PH rate.Especially for fuel gas,FGD devices for media of Ph<000000>ge;4. General suitable for lower acid condition.
		Impeller,Volute Liner, Trhoat Busing,Expeller F.P.L Insert	A33		Abrasion-resistant performance is 20%less than A05.Fair corrosion resistance performance. Oxide slurry with PH rate no less than 1,like phosphogypsum in phosphate fertilizer plant,nitric acid,sulphoacid and phosphoric acid etc.
	45 Carbon Stee	Shaft,Casing Bolt	45	ASTM 1045	Corrosion conditions with low PH rate,especially for fuel gas,FGD devices for media of Ph<000000>ge;4. General suitable for lower acid condition.
	3cr13	Shaft Sleeve, Spacer	3cr13	ASTM420

二、Rubber Materials

For slurries with fine particles and high corrosiveness but low abrasiveness, rubber-lined components are commonly used in Warman pumps. Rubber impellers and liners offer good corrosion resistance and flexibility.

No.	China Code	Parts Names	Warman	U.S.A	Performance&Application
			Code	Code
Rubber	Natural Rubber	Impeller,Volute Liner Trhoat Busing,Expeller, F.P.L Insert	R26		R26 Soft Natrual Rubber used for liners where slurry contains fine particles and more erosive.



	Natural Rubber	Impeller,Volute Liner Trhoat Busing,Expeller, F.P.L Insert	R55		R55 is widely used for impellers,Liners,Bushes. Max particle size can be 20mm,impeller peripheral speed less than 25m/s temperature less than 75°℃.



	EPDM Rubber	Impeller,Volute Liner, Trhoat Busing,Expeller, F.P.L Insert	S01		S01 is widely used for impellers,Liners,Bushes,Max particle size can be 8 mm,impeller peripheral speed less than 25m/s temperature less than 120℃.



	NBR	Impeller,Volute Liner Trhoat Busing,Expeller, F.P.L Insert	S12		S12 is widely used for impellers,Liners,Bushes,Max particle size can be 7 mm,impeller peripheral speed less than 27m/s temperature less than 95℃



	Butyl Rubber	Impeller,Volute Liner, Trhoat Busing,Expeller, F.P.L Insert	S21		S21 is widely used for impellers,Liners,Bushes,Max particle size can be 7 mm,impeller peripheral speed less than 30m/s temperature less than 100℃.



	Hypalon	Impeller,Volute Liner, Trhoat Busing,Expeller, F.P.L Insert	S31		S31 can be used for impellers,Liners,Bushes,it's recommended used for strong acid slurry with mild and moderate corrosion.Max particle size can be 10 mm,,impeller peripheral speed less than 30m/s temperature ess than 110℃.




	Neoprene		S42		Neoprene is high strength synthetic elastomer with dynamic properties slightly inferior to natura rubber.It is less effected by temperature than natural rubber,has excellent weathering and ozone and exhibits oil resistance.
		Impeller,Volute Liner Trhoat Busing,Expeller, F.P.L Insert



Urethane	Polyurethane	Impeller,Volute Liner, Trhoat Busing,Expeller, F.P.L Insert	U01		U01 is an erosion resistant material performs wellwhere tramp'is a problem.This is attributed to the high tear and tensile strength of U01. However,its general erosion resistance is inferior to that of natural rubber(R26,R08).